No. | Crack ID | Test period ID | Observed da/dt (10−8 mm/s) |
---|---|---|---|
1 | 1–3-1 | VII | 2.6 |
2 | 1–3-2 | V | 1.2 |
3 | 1–3-2 | VI | 1.2 |
4 | 1–3-2 | VII | 1.6 |
5 | 1–6-1 | V | 0.7 |
6 | 1–6-1 | VI | 1.2 |
7 | 1–6-2 | V | 2.8 |
8 | 1–6-2 | VI | 2.5 |
9 | 1–6-2 | VII | 6.2 |
10 | 1–6-3 | V | 1.5 |
11 | 1–6-3 | VI | 1.3 |
12 | 1–6-3 | VII | 4.5 |
13 | 1–9-1 | V | 2.5 |
14 | 1–9-1 | VI | 2.5 |
15 | 1–9-2 | V | 2.3 |
16 | 1–9-2 | VI | 3.4 |
17 | 1–12-1 | VI | 0.7 |
18 | 1–12-2 | V | 1.2 |
19 | 2–3-1 | II | 0.9 |
20 | 2–3-1 | III | 0.8 |
21 | 2–3-2 | II | 1.3 |
22 | 2–3-3 | II | 1.2 |
23 | 2–3-3 | III | 0.9 |
24 | 2–3-4 | II | 6.1 |
25 | 2–3-4 | III | 3.0 |
26 | 2–6-1 | II | 0.8 |
27 | 2–6-2 | II | 3.7 |
28 | 2–6-2 | III | 2.4 |
29 | 2–6-3 | II | 0.9 |
30 | 2–6-3 | III | 1.5 |
31 | 2–6-4 | II | 2.6 |
32 | 2–6-4 | III | 2.4 |
33 | 2–12-1 | II | 1.2 |
34 | 2–12-1 | III | 1.1 |
35 | 2–12-2 | II | 2.6 |
36 | 2–12-2 | III | 1.3 |
37 | 2–12-3 | II | 0.5 |
38 | 2–12-4 | II | 4.0 |
39 | 2–12-4 | III | 1.9 |